AlCu4Mg2 鋁合金。擠壓棒材
|
|
|
|
|
|
|
|
|
|
|
編號：ENAW-2024
|
|
|
|
|
|
|
|
|
|
|
分類：鋁-2000系列（銅是主要合金元素）
|
|
|
|
|
|
|
|
|
|
|
標(biāo)準(zhǔn)：EN 573-3:2009鋁和鋁合金。鍛造產(chǎn)品的化學(xué)成分和形式。產(chǎn)品的化學(xué)成分和形式
|
|
|
|
|
|
|
|
|
|
|
EN 755-2:2008鋁和鋁合金。擠壓棒材、管材和型材。機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
EN 485-2:2008鋁和鋁合金。薄板、帶材和板材。機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
EN 754-2:2008鋁和鋁合金。冷拔棒材/棒材和管材。機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
EN 603-2:1997鋁和鋁合金。鍛造坯料。機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
EN 1301-2:1997鋁和鋁合金。拉線。機(jī)械性能
|
|
|
|
|
|
|
|
|
|
|
EN 941:1996鋁和鋁合金。用于一般應(yīng)用的圓形和圓形坯料。規(guī)格
|
|
|
|
|
|
|
|
|
|
|
EN 12392:2000鋁和鋁合金。鍛造產(chǎn)品。壓力設(shè)備生產(chǎn)用產(chǎn)品的特殊要求
|
|
|
|
|
|
|
|
|
|
|
EN 1715-3：2008鋁和鋁合金。提取庫存。機(jī)械用途的具體要求（不包括焊接）
|
|
|
|
|
|
|
|
|
|
|
Chemical comb % of grade AlCu4Mg2
|
|
|
|
|
|
|
|
|
|
|
Zr +Ti < 0.2 may be used for extruded and forged products
|
|
|
|
|
|
|
|
|
|
|
Fe
|
Si
|
Mn
|
Cr
|
Ti
|
Cu
|
Mg
|
Zn
|
Others
|
-
|
|
max 0.5
|
max 0.5
|
0.3 - 0.9
|
max 0.1
|
max 0.15
|
3.8 - 4.9
|
1.2 - 1.8
|
max 0.25
|
each 0.05; total 0.15
|
Al - remainder
|
|
|
|
|
|
|
|
|
|
|
|
|
Mechanical properties of grade AlCu4Mg2
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (O)
|
220
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (O) (H111)
|
250
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (T3)
|
395-450
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rm - Tensile strength (MPa) (T8)
|
455
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (O)
|
140
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (O) (H111)
|
150
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (T3)
|
270-310
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Rp0.2 0.2% proof strength (MPa) (T8)
|
380
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (O) (H111)
|
12
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (T3)
|
8
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation at fracture (%) (T8)
|
5
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (O)
|
12月13日
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (O) (H111)
|
10
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (T3)
|
6
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
A - Min. elongation Lo = 50mm (%) (T8)
|
4
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (O) (H111)
|
47
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (T3)
|
120
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (T8)
|
130
|
|
|
|
|
|
|
|
|
|
Brinell hardness (HBW): (O)
|
55
|
|
|
|
|
|
|
|
|